ERSA selective soldering nozzle 213510 (2.0/4.5, H47,B22)

Bạn đang ở đây: Nhà » Sản phẩm » VÒI PHUN SMT » ERSA selective soldering nozzle 213510 (2.0/4.5, H47,B22)
Số mô hình: 213510
Product Name: Soldering nozzle ERSA
Kích thước: 2.0/4.5, H47,B22
Vật liệu: Titanium alloy+oxide layer
Use for: ERSA selective soldering
Nơi xuất xứ: Thâm Quyến Trung Quốc
Thời gian hoàn thiện: Cổ phiếu
ERSA selective soldering nozzle 213510 (2.0/4.5, H47,B22)

7 tips for users to extend the soldering nozzle’s lifespan.

Why do we need to add an oxide layer?

1. Enhanced Corrosion Resistance
Phát: Titanium alloys may corrode after long exposure to active flux and molten solder.

Oxide Layer Effect:
Anodized TiO₂ layer blocks chemical contact.
Strongly resists halide attack (Cl⁻, Br⁻).
Prevents inner surface roughening.

2. Improved Hardness and Wear Resistance
Phát: Titanium (≈36 HRC) still wears under solder impact.

Oxide Layer Effect:
Hardness increases to 800–1200 HV.
Reduces wear from solder and dross.
Lower friction, less solder sticking.
Longer cleaning intervals.

3. Better High-Temp Oxidation Resistance
Phát: Natural oxide is thin and uneven at 260–300°C.

Oxide Layer Effect:
Dense artificial layer blocks oxygen diffusion.
Prevents nozzle embrittlement.
Less dross buildup; stable wave.

4. Reduced Solder Wettability
Phát: Molten solder wets titanium easily, causing residue.

Oxide Layer Effect:
TiO₂ has low surface energy.
Solder doesn’t stick easily.
Easier to clean.

Các Khoản mục khác trong thể loại này
Biểu mẫu Yêu cầu
Tên: 
 *
Email: 
 *
Quốc gia: 
 *
Thông điệp: 
Xác minh:  2 + 8 = ?
Please enter the answer to the sum & Click Submit to verify your registration.
 
Bản quyền 2008-2026 Thâm Quyến FS thiết bị CO.,LTD Tất cả các quyền được bảo lưu.
Sơ đồ trang web | Trên cùng↑